Dongguan Sen 5052 aluminum and metal materials Co., Ltd. is a world-renowned brand agents aluminum, aluminum coil, aluminum rod and other professional Alcoa aluminum supply of imported brands are: Alcoa ALCOA, Alcan ALCAN, Aleris ALERIS Sumitomo, Nippon Light Metal, Kobe Steel KOBELCO, Korea NOVELIS, Russia KUMZ etc; the supply of domestic brands are: China Aluminum Corporation (a subsidiary of Northeast Light Alloy, SWA, Northwest Aluminum), and other well-known brands. 5052 aluminum for AL-Mg alloy aluminum, is the most widely used as a rust-proof aluminum, high strength of this alloy, especially with anti-fatigue strength Fu: plasticity and high corrosion resistance, heat treatment can enhance the half When the plastic is still good work hardening, work hardening at low plasticity, good corrosion resistance, good weldability, machinability bad, can be polished. 5052 high strength aluminum special ???? point, especially with anti-fatigue strength of Fu ???? nature AL-Mg alloy aluminum application transport vehicles, sheet metal ship name introductory material: Aluminum and aluminum extrusion Pressure Bar (≤150mm, H112, T6, O state) Standard: GB / T3880-2006 Features and Scope: ① 5052 belongs to Al-Mg alloy, using a wide range, especially in the construction industry can not do without this alloy is The most promising alloys. Good corrosion resistance, weldability, cold is better, and with moderate intensity. 5052 is the main alloying elements of magnesium, has good forming properties, corrosion resistance, weldability, moderate intensity, for the manufacture of aircraft fuel tanks, pipelines, and transportation vehicles, ship sheet metal parts, instruments, lights bracket and rivets, metal products, electrical - housing and so on. ② AL-Mn alloy, is the most widely used as a rust-proof aluminum, high strength of this alloy, especially with anti-fatigue strength: high ductility and corrosion resistance, heat treatment can enhance the plastic work hardening in half still good, when the plastic work hardening is low, good corrosion resistance, good weldability, machinability bad, can be polished. Mainly used for high plasticity and good weldability, working in a liquid or gaseous medium low load parts, such as tanks, gasoline or oil conduit, and a variety of other liquid containers made by deep drawing of a small load parts: wire used to make rivets. Applications 5052 aluminum uses mainly used for high plasticity and good weldability, also commonly used in transport vehicles, vessels, sheet metal parts, instruments, lights bracket and rivets, metal products, electrical appliances, such as Shell. Can also be used in the manufacture of aircraft fuel tanks, fuel lines, aerospace aluminum alloy material, is typical of the anti-rust aluminum alloy chemical composition Al: margin; Si Si: 0.25; copper Cu: 0.10; Mg Mg: 2.2 ~ 2.8; Zinc Zn: 0.10; Manganese Mn: 0.10; chromium Cr: 0.15 ~ 0.35; iron Fe: 0.4 0. Mechanical Properties Tensile strength (σb): 170 ~ 305MPa yield strength conditions σ0.2 (MPa) ≥65 modulus of elasticity (E): 69.3 ~ 70.7Gpa annealing temperature: 345 ℃. 5052 aluminum specification for aluminum thickness: 0.15mm-50mm, width: 100mm-2000mm, length: 1000mm-9000mm, aluminum coil thickness: 0.05mm-15mm, width: 15mm-2000mm aluminum Insulation thickness: 0.3mm-0.9 mm Width: 500mm-1000mm Length: Any non-slip aluminum thickness: 1mm-10mm Width: 1000mm-1500mm Length: 2000-3000mm embossed aluminum thickness: 0.1mm-0.9mm Width: 500mm-1200mm Length: Any surface quality 1, surface does not allow cracks, corrosion spots and nitrate traces. 2. Allow the surface defect site where the depth does not exceed the nominal wall thickness of 8% from the size of the skin, bubbles, surface roughness and local super mechanical damage, but can not exceed the maximum defect depth 0.5mm, the total area of ??the defect does not exceed the total area of ??the plate 5%. 3, allows the supplier to the lighting along the longitudinal profile smooth surface. 4. Other requirements: There is a demand side and the supply side drawn up. Welding electrode Model 5052 is available ER5356 aluminum welding rod after welding to meet the mechanical properties of 5052 aluminum. 5356's chemical composition: Si: 0.25; Fe: 0.40; Cu: 0.10; Mn: 0.05-0.20; Mg: 4.5-5.6; Cu: 0.02--0.20; Zn: 0.10- 0.20; Ti: 0.06--0.20; Al : margin; 5336 higher magnesium content. Hardness: 1060 aluminum tensile strength of between 110-130, and 5052 series of tensile strength reached a hardness That hardness than 5052 between 1060 210-230 100 percent higher. Elongation: The elongation of 1060 series of 5%, while the 5052 series of extension rate of between 12-20%, also can be considered, in the 5052 series of the hard case 100% than 1060, the elongation increased by 200 about%. Chemical properties: 1060 pure aluminum, aluminum alloy 5052, 5052 under special circumstances corrosion better. Standard aluminum with national standards (GB / T 3880-2006), unified standards applicable to aluminum strip material.